Structure and properties of (Na0.5Bi0.5)ZrO3 (NBZ) lead-free perovskite compound


The structure of NBZ was studied by neutron diffraction. NBZ is monoclinic, (SG #11 P21/m) am = 5.696(8) Å, bm = 8.166(9) Å, cm = 5.790(4) Å and βm = 89.97(4)°. Being centrosymmetric, NBZ is neither piezoelectric nor ferroelectric. No phase transition was evidenced between 100 K and 923 K. NBZ presents a relaxor behavior below room temperature attributed to the mixed occupancy of the A-site by both Na + and Bi 3+ ions. The relative permittivity of NBZ appears noticeably stable (for 1 kHz-2.9% at-55 °C / 218K and +5.3% at 85 °C / 358 K compared to the 25 °C / 298 K value). NBZ appears thus as promising for the elaboration of capacitors requiring high thermal stability


Fichier principal
Vignette du fichier
Scripta Materiala 2019-161-p13-17.pdf (2.99 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01895309 , version 1 (15-10-2018)



Jerome Lelievre, Michaël Josse, Pascal Marchet. Structure and properties of (Na0.5Bi0.5)ZrO3 (NBZ) lead-free perovskite compound. Scripta Materialia, 2019, 161, pp.13-17. ⟨10.1016/j.scriptamat.2018.10.003⟩. ⟨hal-01895309⟩
99 Consultations
213 Téléchargements



Gmail Facebook X LinkedIn More