Donor–acceptor (D–A) small molecules are regarded as promising hole-transporting materials for perovskite solar cells (PSCs) due to their tunable optoelectronic properties. This paper reports the design, synthesis and characterization of three novel isomeric D-π-A small molecules PY1, PY2 and PY3. The chemical structures of the molecules consist of a pyrazolo[1,5-a]pyrimidine acceptor core functionalized with one 3,6-bis(4,4′-dimethoxydiphenylamino)carbazole (3,6-CzDMPA) donor moiety via a phenyl π-spacer at the 3, 5 and 7 positions, respectively. The isolated compounds possess suitable energy levels, sufficient thermal stability (Td > 400 °C), molecular glass behavior with T$_g$ values in the range of 127–136 °C slightly higher than that of the reference material Spiro-OMeTAD (126 °C) and acceptable hydrophobicity. Undoped PY1 demonstrates the highest hole mobility (3 × 10−6 cm$^2$ V$^{−1}$ s$^{−1}$) compared to PY2 and PY3 (1.3 × 10−6 cm$^2$ V$^{−1}$ s$^{−1}$). The whole isomers were incorporated as doped HTMs in planar n-i-p PSCs based on double cation perovskite FA0.85Cs0.15Pb(I0.85Br0.15)3. The non-optimized device fabricated using PY1 exhibited a power conversion efficiency (PCE) of 12.41%, similar to that obtained using the reference, Spiro-OMeTAD, which demonstrated a maximum PCE of 12.58% under the same conditions. The PY2 and PY3 materials demonstrated slightly lower performance in device configuration, with relatively moderate PCEs of 10.21% and 10.82%, respectively, and slight hysteresis behavior (−0.01 and 0.02). The preliminary stability testing of PSCs is also described. The PY1-based device exhibited better stability than the device using Spiro-OMeTAD, which could be related to its slightly superior hydrophobic character preventing water diffusion into the perovskite layer.