Modification induces by milling on liquid phase sintering. - Université de Limoges Accéder directement au contenu
Article Dans Une Revue Materials Science Forum Année : 1995

Modification induces by milling on liquid phase sintering.


The powders of a W-based alloy have been milled to improve the sintering and increase the density. Either the only second phase NiFeCo has been milled or both the second phase and tungsten. In the same sintering conditions, treated powders show a higher densification in comparison with the untreated powders. To understand this change of behaviour, experiments are carried out at temperatures lower and higher than liquid phase formation. At these temperatures, densities of treated powders are highest. Based on scanning electron microscopy observations, EDS measurements, X-Ray diffraction pattern investigations, we study the influence of the milling on the powders and on the densification before and after the liquid formation.


Chimie Matériaux
Fichier non déposé

Dates et versions

hal-01880512 , version 1 (25-09-2018)


  • HAL Id : hal-01880512 , version 1


Claire Chausse, Françoise Nardou, Gaffet Eric. Modification induces by milling on liquid phase sintering.. Materials Science Forum, 1995, 179-181, pp.391-396. ⟨hal-01880512⟩
24 Consultations
0 Téléchargements


Gmail Facebook X LinkedIn More