Oxygen semi-permeation properties of La 1− x Sr x FeO 3−δ perovskite membranes under high oxygen gradient

Résumé

This work is focused on the evaluation of oxygen semi-permeation and electrochemical performances under high oxygen gradient of free cobalt perovskite membrane materials; La 1− x Sr x FeO 3−δ perovskite. For a better understanding of oxygen transport through La 1− x Sr x FeO 3−δ perovskite membranes, the oxygen diffusion, oxygen incorporation, and desorption coefficients were determined under high oxygen gradient in relation to the temperature for La 1− x Sr x FeO 3−δ (with x = 0.1, 0.3, 0.5, and 0.7) by a specific method based on oxygen semi-permeation. The best electrochemical performances were obtained for La 0.3 Sr 0.7 FeO 3−δ (LSF37) and La 0.5 Sr 0.5 FeO 3−δ (LSF55) perovskite membranes with oxygen fluxes of 1.7 × 10 −3 and 1.2 × 10 −3 mol/m 2 s at 900 °C, respectively. The oxygen incorporation and desorption coefficients of LSF55 were two times lower than those of LSF37 and similar to those of La 0.5 Sr 0.5 Fe 0.7 Ga 0.3 O 3−δ . The values of these coefficients are discussed and compared with the data reported in the literature by isotopic exchange for the similar material compositions.
Fichier principal
Vignette du fichier
Oxygen semi-permeation properties of La1-xSrxFeO3-δ perovskite membranes under high oxygen gradient.pdf (1.13 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03219398 , version 1 (06-05-2021)

Identifiants

Citer

Eva Deronzier, Thierry Chartier, Pierre-Marie Geffroy. Oxygen semi-permeation properties of La 1− x Sr x FeO 3−δ perovskite membranes under high oxygen gradient. Journal of Materials Research, 2020, 35 (18), pp.2506-2515. ⟨10.1557/jmr.2020.230⟩. ⟨hal-03219398⟩
44 Consultations
123 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More