Aging behavior in Co doped barium titanate ceramics


BaTiO 3 ceramics were doped with acceptor metallic ions (Co, Mn, Fe) and co-doped with Co and Nb. Piezoelectric ceramics were prepared using conventional solid-state reaction. Addition of Li 2 O sintering aid allows obtaining dense ceramics at low sintering temperature. Doping with Co acceptor leads to significant improve of piezoelectric properties but induce distorted and shifted hysteresis loop due to the presence of internal bias field. Field cooling poled ceramics are in the aged state just after poling. Increasing acceptor dopant concentration increases the internal bias field while co-doping with donor (Nb) reduces it. The data are consistent with presence of defect dipoles formed by acceptor substituted in B site and oxygen vacancy of BaTiO 3 tetragonal structure. Alignment of defect dipoles along driven electric field was observed through low frequency switching or cycling. Aging behaviors of unpoled and poled ceramics process were investigated through the study of hysteresis loops and reveal that charge compensation is not complete
Fichier principal
Vignette du fichier
Proceedings_ISAF_2016_v4.pdf (476.76 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01878807 , version 1 (24-09-2019)



Rémy Ul, Mai Pham-Thi, Pascal Marchet. Aging behavior in Co doped barium titanate ceramics. 2016 Joint IEEE International Symposium on the Applications of Ferroelectrics, European Conference on Application of Polar Dielectrics, and Piezoelectric Force Microscopy Workshop (ISAF/ECAPD/PFM), Aug 2016, Darmstadt, Germany. ⟨10.1109/ISAF.2016.7578061⟩. ⟨hal-01878807⟩
53 Consultations
264 Téléchargements



Gmail Facebook X LinkedIn More